Aluminium Tig Rod 5356

4043 has lower shear strength than that of 5356 see fig 1.

Aluminium tig rod 5356.

Boc 5356 tig rod is a nominal 5 magnesium alloy suitable for tig welding of a wide range of cast and wrought aluminium alloys. 36 40 1 16 1 6mm. Common applications are welding of boats ships bicycles tanks pressure vessels and automotive. Typically when gas metal arc welding gmaw feedability will become a less critical issue when feeding the more rigid 5356 alloy.

12 16 1 8 3 2mm. Alloy 5356 weld data sheet typical applications welding filler wire general information trade designation. Magnesium manganese chromium titanium moderate high strength capabilities. This may be of consideration when calculating the size of fillet welds.

Er5356 high quality washington alloy brand aluminum magnesium cut length tig filler metal. Pack for each diameter. Ok tigrod 5356 is the most widely used welding alloy and can be classified as a general purpose type filler alloy. Almigweld and altigweld non heat treatable similar to almg5 din en iso designation almg5cr a principle alloying elements.

Alloy 5356 is an all position non heat treatable tig wire used to weld the 5xxx series alloys when 40 000 psi tensile strength is not a requirement. 4043 is a softer alloy in the form of spooled wire when compared to 5356. 26 30 3 32 2 4mm. Alloy 5356 is an all position non heat treatable tig wire used to weld the 5xxx series alloys when 40 000 psi tensile strength is not a requirement.

Aws a5 10 grade class er5356 available diameters 045 1 16 3 32 1 8 length 36 914mm weight 1 lb. Tig welder filler rods and tig welding wire for aluminium 5356 grade in a choice of pack sizes high quality tig wire filler rods buy online for next day delivery. Alloy 5356 tig description. Approximate number of rods per 1lb.

8 10 note. Ok tigrod 5356 is typically chosen because of its relatively high shear strength. The 5xxx alloy base material welded with ok tigrod 5356 with a weld pool chemistry greater than 3 mg and service temperatures in excess of 65 c are susceptible to stress corrosion cracking.